Chemical Resistant Chlorinated Rubber Based Enamel Supplier in China
Chemical Resistant Chlorinated Rubber Based Enamel paint coating manufacture Shenzhen China  
Home About Us Products Contact Us

 

 




Honest Joy Coating & Paint
Vinyl Coating

Chemical Resistant Chlorinated Rubber Based Enamel
Chlorinated Rubber Based Anti-corrosive Primer
Chlorinated Rubber Swimming Pool Paint
Chlorinated Rubber Enamel

Chlorinated Rubber High Build Coating
Economical Anticorrosive Chlorinated Rubber Based Primer
Tintable Chlorinated Rubber Finish
Polychloroprene Rubber Solvent Based Primer
Phisically Drying Modified Chlorinated Rubber Based Primer
General Purpose Chlorinated Rubber Primer
Chlorinated Rubber Intermediate Coating

Chlorinated Rubber Micaceous Iron Oxide coating
Premium Quality Full-bodied Smooth-flowing Vinyl-acrylic Primer
Abrasion Resistant Vinyl Ester Coating
Catalyzed Vinyl Ester Primer
Chlorinated Rubber Based Intermediate Coat

Chlorinated Rubber MIO Intermediate Coating

  

Chemical Resistant Chlorinated Rubber Based Enamel

PRODUCT SPECIFICATIONS:

DESCRIPTION
A chemical resistant chlorinated rubber based enamel for interior/exterior protection of metal and concrete substrates. It provides severe chemical and moisture resistance with superior adhesion to these substrates.
RECOMMENDED USES
For use over prepared steel, iron, aluminum, and galvanized metal, concrete block, paper mills, laundries, food processing, dairies.
CHARACTISTICS
Color:
Wide range of colors
Finish:
Semigloss
Volume Solid:
34% +1%
Specific Gravity:
1.19 KGs / ltr + 2%
Recommended DFT:
75 Microns
Spreading Rate@DFT:
4.53 m/ ltr or
17.16 m/ gallon
Flash Point:
26 C
Drying Schedule:
Dry to Touch:
15 Minutes
@ 25 oC/R.H.50
To Handle:
2 Hours
To Recoat:
1 Hour
Shelf Life:
18 months, unopened at 25 oC
Reducer/Clean Up:
Industrial thinner HJ-09
APPLICATION PROCEDURES
Surface Preparation:Surface must be dry, clean and in sound condition. Remove oil, dust, dirt, millscale or other foreign substance to ensure good adhesion. Minimum surface preparation methods to be followed for (1) Iron and Steel – SSPC-SP2 or SP3 (2) Aluminum and Galvanizing – SSPC-SP1. (3) Concrete should be well cured before applying. Allow weathering of new galvanized steel for six months prior to coating.
Application Methods:
Conventional Spray:
Reduce 10% with industrial thinner
Airless Spray:
Reduce 10% with industrial thinner
Brush/Roller:
Reduction not recommended
SYSTEM RECOMMENDATION
Iron and Steel:
Hi-Build Chlorinated Rubber Primer
1 Coat
75 Microns DFT
Hi-Build Chlorinated Rubber Enamel
2 Coats
75 Microns DFT
per coat
Aluminum and Galvanized Metal:
Wash Primer Green
1 Coat
07 Microns DFT
Hi-Build Chlorinated Rubber Primer
1 Coat
75 Microns DFT
Hi-Build Chlorinated Rubber Enamel
2 Coats
75 Microns DFT
per coat
Concrete Block/Masonry Surface:
Recommended Primers/Fillers
1 Coat
As Recommended
Hi-Build Chlorinated Rubber Enamel
2 Coats
75 Microns DFT
per coat
Recommended Primers/Fillers:
• Epoxy Clear Primer Sealer
• Cati-Coat Epoxy Filler Sealer
• Hi-Build Chlorinated Rubber Primer
• Acrylic Primer Sealer (S) or (W)

SPECIAL TIPS
Excessive reduction of material can affect the film build, appearance, and adhesion.
SAFETY PRECAUTIONS
Spray under well-ventilated conditions. Do not breathe or inhale mist. When spraying, wear air mask. Avoid skin contact. Spillage on skin should immediately be removed with suitable cleanser, soap and water. Eyes should be flushed with water and medical attention sought immediately.

 

 