Chlorinated Rrubber Based Anti-corrosive Primer Supplier in China
Chlorinated Rrubber Based Anti-corrosive Primer paint coating manufacture Shenzhen China  
Home About Us Products Contact Us

 

 




Honest Joy Coating & Paint
Vinyl Coating

Chemical Resistant Chlorinated Rubber Based Enamel
Chlorinated Rubber Based Anti-corrosive Primer
Chlorinated Rubber Swimming Pool Paint
Chlorinated Rubber Enamel

Chlorinated Rubber High Build Coating
Economical Anticorrosive Chlorinated Rubber Based Primer
Tintable Chlorinated Rubber Finish
Polychloroprene Rubber Solvent Based Primer
Phisically Drying Modified Chlorinated Rubber Based Primer
General Purpose Chlorinated Rubber Primer
Chlorinated Rubber Intermediate Coating

Chlorinated Rubber Micaceous Iron Oxide coating
Premium Quality Full-bodied Smooth-flowing Vinyl-acrylic Primer
Abrasion Resistant Vinyl Ester Coating
Catalyzed Vinyl Ester Primer
Chlorinated Rubber Based Intermediate Coat

Chlorinated Rubber MIO Intermediate Coating

  

Chlorinated Rrubber Based Anti-corrosive Primer

PRODUCT SPECIFICATIONS:

CHLOROKOTE ZINC PHOSPHATE PRIM GREY / RED
A chlorinated rubber based anti-corrosive primer containing zinc phosphate pigment. When top
coated with finish, the coating system exhibits superb water impermeability and
resistance to acid fumes. An economical coating system for structural steel, equipments etc, in
coastal and chemical environment. This red version contains red oxide of iron apart from zinc
phosphate pigment.

 

Colour

Grey / Red Oxide

STEEL SURFACES:

Finish

Matt to Egg Shell

Surface should be perfectly clean and dry before applying Zinc Phosphate Primer.

Flash Point:

Above o C

 

Volume Solids:

38 % approximately

 

Recommended dry film thickness

30 -40 microns per coat.

 

Corresponding wet film thickness:

79 -105 microns

APPLICATION DETAILS

Method of application: Airless spray / Brush / Roller Notes on Airless Spray: Tip Range: 18 -26 thou Total out put fluid pressure-2700 -3500 psi (190 -246 kg/sq.cm) Thinner: Specified thinner

Theoretical Spreading Rate

12.7 –9.5 Sq.metre per litre

 

Drying time

Touch dry-1/2 hours Hard dry-6 -8 hours

 

Interval before Overcoating

Minimum – 8 hours Maximum – indefinite

LIMITATIONS

Coating not resistant to solvents, oils, grease and fats. The film is thermoplastic and is liable to soften and decompose above 65o C

Storage life

Upto 12 months so long as the material is stored in sealed containers under standard warehouse storage conditions.

USES

Structural Steel, Pulp & Paper Mills, Chemical Plants, Bridges, Jetties, Pipelines, Tank Farms, Fertilizer Plants, Marine Installations.

Dry Heat Resistance

Upto 65o C (Intermittent)

CHEMICAL RESISTANCE GUIDE (With suitable top coat)

EXPOSURE

SPLASH &
SPILLAGE

FUMES & OUTDOOR
EXPOSURE

Acids

Good

Very Good

Alkalis

Fair

Fair

Solvents

Poor

Poor

Salt

Good

Good

Water

Very Good

Very Good

NOTES
1. This cancels all previous literature on this product and is subject to revision without notice
2. Do not apply when temperature falls below 10o C or rises above 50o C and when relative
humidity rises above 90%. Do not apply during rain, fog or mist.
3. Primed steel works should not be exposed for a long period and should preferably be coated
with suitable topcoats at the earliest.
HEALTH AND SAFETY
Please refer to the separate safety data sheet available with detailed information.
PRECAUTION
Provide adequate ventilation during painting. Avoid over-brushing of the product.

 