Chlorinated Rubber Enamel Supplier in China
Chlorinated Rubber Enamel paint coating manufacture Shenzhen China  
Home About Us Products Contact Us

 

 




Honest Joy Coating & Paint
Vinyl Coating

Chemical Resistant Chlorinated Rubber Based Enamel
Chlorinated Rubber Based Anti-corrosive Primer
Chlorinated Rubber Swimming Pool Paint
Chlorinated Rubber Enamel

Chlorinated Rubber High Build Coating
Economical Anticorrosive Chlorinated Rubber Based Primer
Tintable Chlorinated Rubber Finish
Polychloroprene Rubber Solvent Based Primer
Phisically Drying Modified Chlorinated Rubber Based Primer
General Purpose Chlorinated Rubber Primer
Chlorinated Rubber Intermediate Coating

Chlorinated Rubber Micaceous Iron Oxide coating
Premium Quality Full-bodied Smooth-flowing Vinyl-acrylic Primer
Abrasion Resistant Vinyl Ester Coating
Catalyzed Vinyl Ester Primer
Chlorinated Rubber Based Intermediate Coat

Chlorinated Rubber MIO Intermediate Coating

  

Chlorinated Rubber Enamel

PRODUCT SPECIFICATIONS:

Product Description
HJ-070 is a high performance coating based on plasticized chlorinated rubber and suitably
pigmented for heavy-duty protection in severe moisture and chemical laden environments.
Features and Benefits
· Easy to apply and can be applied via airless spray, conventional spray and brush.
· While inferior surface preparation can never be recommended, HJ-070 has shown to
tolerate though with shorter life, power-tool and hand-cleaned steel.
· Renders hard, inert film showing excellent resistance towards dilute acids, alkalis, certain salts,
oxidizing agents, aliphatic hydrocarbons, alcohols, mineral oils, greases etc.
· Has fast dry and spray re-coat times.
· Does not support mold and fungus growth.
· Can be used in conjunction with cathodic protection. Possesses the required chemical resistance
to withstand alkaline conditions of cathodic conditions.
· The dried coating film has been found to be non-flammable and non-toxic and shown high
electrical resistance.
· Has very low water and water vapour permeability.
· Suitable for varied end applications i.e. ideal for high humidity, moisture, marine atmospheres,
heavy rains, high temperatures, damp conditions, very dusty and fungus prone conditions.
· Impart excellent inter-coat adhesion even on aged coating surfaces.
· Extremely durable and weather resistant with longer maintenance-free life.
· Safe and minimum pollutant.
· Exhibit excellent solvent release properties during film drying.
Recommended uses:
Fertilizer plants handling ammonium and
alkaline salts, nitrates, sulfates, phosphates
and nitric acid fumes.
Sewage farms where hydrogen sulfide and
humidity are present.
Concrete Storage Tanks Water Treatment Plants where high humidity
prevails.
Structural Steel Galvanized Iron
Bleacheries and laundries Breweries
Pulp and Paper Mills Chemical Plants
Marine and shore installations Swimming Pools
Food Processing Plants Areas of excessive moisture
Resistance Guide:
Immersion Resistance @ 30° C
· Fresh and Sea Water
Resistance to spillage and splash - not immersion
· Inorganic salt solutions, alcohols, fresh water, sulfur dioxide fumes : Severe
· Solvents, fuels, animal and vegetable oils and fats : Not Recommended
· Weak solutions of acids, cutting oils, aldehydes, chlorine gas : Severe
· Oxygenated Solvents : Moderate
Surface Preparation:
Steel - The surface should be blast cleaned to SSPC-SP 10-63T . loose rust and scales,
dirt, grease, oil, paint, wax, weak oxide films and other contaminants should be removed. Blast cleaning to
SSPC-SP 5-63 is recommended where heavy corrosive conditions exist or coating is
required to be immersed. That means a surface with a grey metallic colour, slightly roughened to form a
suitable anchor pattern for coatings. This surface is free of all oil, grease, dirt, mill scale, rust, corrosion
products, oxides, paint and other foreign matter. In absence of blast cleaning, prepare the metal surface by
wire brushing, sanding, grinding, scrapping or chipping with hand or power tools. Remove all the
contaminants.
Galvanized Iron - Remove dirt, dust, oil, old paint etc. Degrease the surface with degreasing solvents like
xylene or tri-chloroethylene. Apply one coat of HJ-112 Wash Primer for obtaining maximum
adhesion.
Concrete: Concrete surfaces should be grey or grey-white color and free from pits, pockets and holes.
Prepare the surface with abrasive blasting or power tools. Surface imperfections should be filled in with
DURAPATCH. No cement dust or sand should be dislodged. In absence of blasting, etch the surface with
10-15% muriatic acid diluted in water. Allow this acid solution to remain on the surface for 10-15 minutes or
until the bubbling stops. Thoroughly rinse the floor with water to remove all traces of acid. Allow the floor to
dry completely before painting.

 

TECHNICAL DATA

Name/Description

HJ-070

Type

Single pack cold cured

 

 

Composition

Chlorinated rubber suitably pigmented.

Colour

Range of selected colors.

Finish

Smooth and Glossy

Volume Solids

35 ± 3%

Dry film thickness per coat

30 to 40 microns

Coverage-(theoretical-no loss)

11.67 to 8.75 m² /litre

Serviceability @ 30°C

 

- Dry to touch

30 minutes

- Re-coat by Spray

2 hours

- Re-coat by Brush

16 -24 hours

- Full Cure

7 days

Relative Humidity

90%

Application Temperature

 

- minimum

4°C

- maximum

35°C

 

 

Dry heat resistance

65°C

 

 

Solvent/Thinner

Specified thinner

Flash Point

23°C

Packing

4 & litres

Shelf Life

6 months

 

Flammable. Keep away from heat and open

Precaution

flame. Maintain good ventilation and avoid breathing vapours.

Product Limitation:
HJ-070 is not resistant to most solvents, animal and vegetable oils and fats common in dairies,
packinghouses and sewage treatment facilities. Do not use on floors.
Recommended Systems:
Steel: Moderate Service
Total DFT 110-130 microns
1 coat HJ-500 Chlorinated Rubber High Build Primer @ 50 microns per coat
2 coats HJ-070 Chlorinated Rubber Enamel @ 30-40 microns per coat
Steel: Severe Service
Total DFT 185-5 microns
1 coat HJ-500 Chlorinated Rubber High Build Primer @ 50 microns per coat
1 coat MIO Chlorinated Rubber MIO @ 75 microns per coat
2 coats HJ-070 Chlorinated Rubber Enamel @ 30-40 microns per coat
Galvanized Iron / Aluminium: Moderate Service
Total DFT 118-138 microns
1 coat Anuprime-291 Wash Primer @ 8 microns per coat
1 coat HJ-500 Chlorinated Rubber High Build Primer @ 50 microns per coat
2 coats of HJ-070 Chlorinated Rubber Enamel @ 30-40 microns per coat
Galvanized Iron / Aluminium: Severe Service
Total DFT 193-213 microns
1 coat Anuprime-291 Wash Primer @ 8 microns per coat
1 coat HJ-500 Chlorinated Rubber High Build Primer @ 50 microns per coat
1 coat MIO Chlorinated Rubber MIO @ 75 microns per coat
2 coats of HJ-070 Chlorinated Rubber Enamel @ 30-40 microns per coat
Concrete:
Total DFT 110-140 microns
1 thin coat of HJ-070 Chlorinated Rubber Enamel @ microns per coat
3 coats of HJ-070 Chlorinated Rubber Enamel @ 30-40 microns per coat
Notes
· Brushes and spray equipments should be cleaned with Specified thinner.
· The contents should be stirred thoroughly prior to use.
· When overcoating the weathered or aged HJ-070, ensure that the coating is fully free from
all contamination such as oil, dust, grease, stains etc.
· This coating should always be thinned with Specified thinner. The use of alternative thinners can
severely inhibit the curing mechanism of the coating.
Disclaimer:
Information provided herein is based upon tests believed to be reliable. It does not guarantee the results to
be obtained. Nor does it make any express and implied warranty or merchantability, or fitness for a
particular purpose concerning the effects or results of such case. It does not release you from the
obligation to test the products supplied by us as to their suitability for the intended uses. The application,
surface preparation and use of the products are beyond our control and, therefore, entirely your own
responsibility.

 