Epoxy Polyamide Anticorrosive High Performance Primer Supplier in China
Epoxy Polyamide Anticorrosive High Performance Primer Coating paint coating manufacture Shenzhen China  
Home About Us Products Contact Us

 

 




Honest Joy Coating & Paint
Zinc primer.htm

Zinc-rich Ethyl Silicate Based Coating
Zinc Silicone Primer Heat Resistant to 500F
Zinc Rich Epoxy Primer
Zinc Rich Epoxy Cold Galvanising Coating

Zinc Phosphate Primer
Zinc Phosphate High Build Anticorrosive Primer-Finish
Zinc Ethyl Silicate Primer
Zinc Chromate metal Primer
Weldable Modified Zinc Ethyl Silicate Pre-fabrication Primer
Two-component Zinc Rich Epoxy Primer
Surface Tolerant Reinforced Inorganic Zinc Primer

Solvent-borne Self-curing Inorganic Zinc Silicate Primer
Reinforced Inorganic Zinc Primer
Chlorinated Rubber Zinc Rich Coating

Epoxy Zinc Phosphate Iron Oxide Primer
Epoxy Polyamide Anticorrosive High Performance Primer

Fast Drying Low VOC Zinc Rich Epoxy Primer

Inorganic Hybrid Zinc Rich Protective High Temperature Primer
Quick Dry High Performance Zinc Phosphate Primer
Free Low VOC Rreinforced Inorganic Zinc Primer
Solvent-borne Self-curing Inorganic Zinc Silicate Coating



  

PRODUCT SPECIFICATIONS:

Product Description
HJ-707Pis a two-component epoxy polyamide anticorrosive high performance primer containing
zinc chrome as rust inhibitive pigment. It cures to a tough and highly rust preventive coat.
Features and Benefits
· Easy to apply and can be applied via airless spray, conventional spray, brush or roller.
· Ideal for use as a field primer on interior and exterior steel as part of a system to be topcoated with
chlorinated rubber, epoxy and polyurethane topcoats.
· A rust inhibitive primer over iron and steel and protects steel from atmospheric corrosion.
· Provides much higher degree of protection than conventional primers in severe corrosive
conditions.
· Excellent resistance to acids, alkalis, water, salts, oils, petroleum solvents.
· Has very low water and water vapour permeability.
· Has excellent adhesion, toughness, abrasion resistance and overall chemical and solvent
resistance.
· While inferior surface preparation can never be recommended, HJ-707Pcan tolerate,
though with shorter life, power tool and hand cleaned steel surfaces.
· Ideal for high humidity, moisture, marine atmospheres, heavy rains, high temperatures, damp
conditions, very low dusty and fungus prone conditions.
· Durable and economical.
Recommended uses

Blasted Steel structures

Off-shore structures

Pipelines Power Plants

Fertilizer Plants Marine & Shore Installations

Surface Preparation
Steel - The surface should be blast cleaned to SSPC-SP 10-63T . loose rust and scales,
dirt, grease, oil, paint, wax, weak oxide films and other contaminants should be removed. Blast cleaning to
SSPC-SP 5-63 is recommended where heavy corrosive conditions exist or coating is
required to be immersed. That means a surface with a grey metallic colour, slightly roughened to form a
suitable anchor pattern for coatings. This surface is free of all oil, grease, dirt, mill scale, rust, corrosion
products, oxides, paint and other foreign matter. In absence of blast cleaning, prepare the metal surface by
wire brushing, sanding, grinding, scrapping or chipping with hand or power tools. Remove all the
contaminants. Apply one coat of HJ-707P. It can be overcoated with Durapoxy 0 Epoxy
Enamel, Anuthane Enamel Polyurethane or Monocoat Enamel Polyurethane, HJ-070
Chlorinated Rubber Enamel.
Non-ferrous Metals- Remove dirt, dust, oil, old paint etc. Degrease the surface with degreasing solvents
like xylene or tri-chloroethylene. Apply one coat of HJ-292 Wash Primer for obtaining maximum
adhesion. Apply one or two coats of HJ-707P.
TECHNICAL DATA

Name/Description

EZC 500

Type

Two pack cold cured

Composition

Epoxy / Zinc Chrome

Colour

Yellow

Finish

Smooth and Matt

Volume Solids (mixed)

44± 3%

Mixing Ratio

Base : Hardener 3 : 1 by volume

Pot Life @ 30°C

6 to 8 hours

Dry film thickness per coat

25 to 30 microns

Coverage-(theoretical-no loss)

17.6 to 14.6 m² /litre

Serviceability @ 30°C

 

Dry to touch

1 hour

Hard Dry

Overnight

Recoat

24 hours

Full Cure

7 days

Induction (Sweat-in-time) @ 30°C

30 minutes

Dry heat resistance

1°C

Relative Humidity

90%

Application Temperature

 

-minimum

10°C

-maximum

35°C

Solvent/Thinner

Specified Thinner

Flash Point

25°C

Packing

4 & litres

Shelf Life

6 months

 

Flammable. Keep away from heat and open

Precaution

flame. Maintain good ventilation and avoid

 

breathing vapours.

Notes:
· Brushes and spray equipments should be cleaned with Our Epoxy Thinner.
· The contents should be stirred thoroughly prior to use.
· After mixing Base and Hardener in recommended proportions, allow for 30 minutes induction
period or sweat-in-time (maturing) before application.
· When overcoating the weathered HJ-707P, ensure that the coating is free from all
contamination like oil, dust, grease, grease stains.
· This coating should always be thinned with Honest joy Epoxy Thinner. The use of alternative
thinners can severely inhibit the curing mechanism of the coating.
Disclaimer:
Information provided herein is based upon tests believed to be reliable. It does not guarantee the results to
be obtained. Nor does it make any express and implied warranty or merchantability, or fitness for a
particular purpose concerning the effects or results of such case. It does not release you from the
obligation to test the products supplied by us as to their suitability for the intended uses. The application,
surface preparation and use of the products are beyond our control and, therefore, entirely your own
responsibility.

 