Free Glass Flake Reinforced Polyester Coating Supplier in China
Free Glass Flake Reinforced Polyester Coating Coating paint coating manufacture Shenzhen China  
Home About Us Products Contact Us

 

 




Honest Joy Coating & Paint
Polyester Coating

TGIC Free Polyester Powder Coating
Reinforced Trowel Applied Polyester Lining Topping
Polyester Thick Film Coating
Polyester Flake Coating

Polyester Resin Fast Setting Bedding Mortar
Polyester Baking Enamel
High Quality Acrylic Polyester Resin Basecoat
Free Glass Flake Reinforced Polyester Coating
Flowable Rapid Setting Polyester Resin Mortar
Flake Filled Polyester Coating
Durable Polyester Powder Coating

Clear Polyester Powder Coating
Abrasion Resistant Glass Flake Reinforced Polyester Coating
Abrasion Resistant Glass Flake Reinforced Polyester Coating




  

PRODUCT SPECIFICATIONS:

Product description
Free Glass Flake Reinforced Polyester Coating is a quick curing, high build, abrasion resistant styrene Free Glass Flake Reinforced Polyester Coating ,
that gives long time corrosion protection.
Recommended use
Steel structures in general and in particular items subject to extreme mechanical wear. May also be used for protection
of aluminium and concrete (special designed systems). Free Glass Flake Reinforced Polyester Coating can be applied as a non-skid coating system
for walkways, escape routes and deck areas.
Film thickness and spreading rate
Minimum Maximum Typical
Film thickness, dry (μm) 600 1500 1000
Film thickness, wet (μm) 610 1530 10
Theoretical spreading rate (m²/l) 1,63 0,65 0,98
Comments
The practical spreading rate may vary from the theoretical dependent upon film thickness and the ambient temperature,
ventilation/wind during the application.
Physical properties
Colour Limited number
Solids (vol %)* 98 ± 1
Flash point 53ºC ± 2
VOC gms/ltr .
Gloss Semiflat
Gloss retention Good
Water resistance Excellent
Abrasion resistance Excellent
Solvent resistance Very good
Chemical resistance Very good
Flexibility Limited
Compatibility with
cathodic protection Very good

Surface preparation
All surfaces should be clean, dry and free from contamination. The surface should be assessed and treated in
accordance with .
Bare steel
Blast cleaning to Sa 2½. . Roughness: using abrasives suitable to achieve a coarse surface of Grade
Medium G (50-85μm, Ry5)
Other surfaces
The coating may be used on other substrates. Please contact your local HONEST office for more information.
Condition during application
The temperature of the substrate should be minimum 5°C and at least 3°C above the dew point of the air, temperature
and relative humidity measured in the vicinity of the substrate. Good ventilation is usually required in confined areas to
ensure proper drying. The coating should not be exposed to oil, chemicals or mechanical stress until fully cured.
Application methods
Spray Preferably 2-comp. airless spray. Application with 1-comp. ordinary airless spray is also possible,
provided that inhibitor is added.
Brush Recommended for stripe coating and small areas, care must be taken to achieve the specified dry
film thickness.
Application data
Mixing ratio (volume) 2-comp. airless spray:
1,25 vol.% 13 at temperatures 10 - 35° C.
2,5 vol.% 13 at temperatures 5 - 10° C.
1-comp. ordinary airless spray:
Addition of inhibitor and peroxide according to table on page 3.
1 can be used instead of 13 at temperatures above 15º C.
Pot life (23°C) 15- minutes (Reduced at higher temperatures).
After addition of inhibitor for 1-comp. ordinary airless spray: 35 minutes.
Thinner Vinyl toluene. If needed max. 5% vinyltoluene.
Cleaner HONEST Thinner No. 17 or HONEST Thinner No 27.
Guiding data airless spray
Pressure at nozzle 15 - 25 MPa (150-250 kp/cm², 2100-4000 psi.)
Ratio/Capacity: >45:1, min. 12 l per minute. Slow moving piston.
Nozzle tip 0,69 - 1.09 mm (0.027 - 0.043'').
Spray angle 40-80°, best 60°.
Filter To be removed.
Ratio/Capacity:
Note For further details please see separate "Working Manual".
Approved alternatives to peroxide 13. can be used. Contact HONEST,
Technical Service Department.
Drying time
Drying times are generally related to air circulation, temperature, film thickness and number of coats, and will be
affected correspondingly. The figures given in the table are typical with:
* Good ventilation (Outdoor exposure or free circulation of air)
* Typical film thickness
* One coat on top of inert substrate
Using 2-comp. airless spray
Substrate temperature 5°C 10°C 23°C 40°C
Surface dry 2.5 h 2.5 h 45 min 45 min
Through dry 2.5 h 2.5 h 45 min 45 min
Cured 3 d 2 d 12 h 4 h
Dry to recoat, minimum 2.5 h 2.5 h 45 min 45 min
Dry to recoat, maximum 1 14 d 14 d 14 d 14 d
Using 1-comp. airless spray
Substrate temperature 10°C 23°C 40°C
Surface dry 3 h 2 h 2 h
Through dry 3 h 2 h 2 h
Cured 3 d 2 d 1 d
Dry to recoat, minimum 3 h 2 h 2 h
Dry to recoat, maximum 1 14 d 14 d 14 d
1. The surface should be free from chalking and contamination prior to application. If the maximum dry to recoat time
is exceeded, please contact HONEST for advice.
The given data must be considered as guidelines only. The actual drying time/times before recoating may be shorter or
longer, depending on film thickness, ventilation, humidity, underlying paint system, requirement for early handling and
mechanical strength etc. A complete system can be described on a system sheet, where all parameters and special
conditions could be included.
Typical paint system
Free Glass Flake Reinforced Polyester Coating 1 x 900 - 1100 μm (Dry Film Thickness)
or
Free Glass Flake Reinforced Polyester Coating 2 x 600 - 750 μm (Dry Film Thickness)
Other systems may be specified, depending on area of use
MIXING RATIO BY USE OF 1-COMPONENT AIRLESS SPRAY
Temperature of steel and paint should not be lower than 10ºC.

Steel and paint temp. ºC

Addition of Inhibitor 9851

Addition of 13

 

Volume percent

ml. into 16 litres of

Volume percent

ml. into 16 litres of

 

 

 

Free Glass Flake Reinforced Polyester Coating

 

Free Glass Flake Reinforced Polyester Coating

 

10 - 15

0.6

96

1.25

0

 

15 -

1.25

0

1.25

0

 

- 25

1.8

290

1.25

0

 

25 - 30

2.5

400

1.25

0

 

30 - 35

3.1

500

1.25

0

 

The temperature of the paint should never be more than 5ºC higher than the steel temperature. The inhibitor should be
mixed thoroughly with Free Glass Flake Reinforced Polyester Coating before adding the required amount of 13. Mechanical agitation
for one minute or more is necessary to secure proper mixing of peroxide with the main component.
Note: Check temperature of pump during application. Friction in piston may cause increase in temperature. If this
should happen, keep pump going to get heated Free Glass Flake Reinforced Polyester Coating out as quickly as possible, and then wash the
equipment.
Storage
The product must be stored below 25°C and in accordance with national regulations. Storage conditions are to keep
the containers in a dry, cool, well ventilated space and away from source of heat and ignition. Containers must be kept
tightly closed.
SHELF LIFE: 6 months, at 23°C, subject to re-inspection therafter. Shelf life very much depends on tempeature. Lower
temperatures (if possible below freezing point) will lengthen the shelf life considerably, while high temperature may lead
to gelling in the tin.
Handling
Handle with care. Avoid that it comes in contact with combustible materiales. Accelerator and peroxide
must never be mixed directly together.
Packing size
litre unit: 16 litres in a litre container
Health and safety
Please observe the precautionary notices displayed on the container. Use under well ventilated conditions. Do not
breathe or inhale mist. Avoid skin contact. Spillage on the skin should immediately be removed with suitable cleanser,
soap and water. Eyes should be well flushed with water and medical attention sought immediately.
For detailed information on the health and safety hazards and precautions for use of this product, we refer to
the Material Safety Data Sheet.
DISCLAIM
The information in this data sheet is given to the best of our knowledge based on laboratory testing and practical
experience. However, as the product is often used under conditions beyond our control, we cannot guarantee anything
but the quality of the product itself. We reserve the right to change the given data without notice.

 