Honest Joy Coating & Paint
Alkyd coating

Urethane-Modified Alkyd Primer
Urethane Alkyd Enamel
Urethane Alkyd Based Toopcoat
Epoxy Ester Modified Alkyd Primer

Superior Quality Alkyd Glaze
Speedy-Dry Alkyd Enamel
Silicone Modified Alkyd Enamel
Semi-Transparent Organic Solvent Stain
Rust-Inhibitive Patented Acrylic Modified Alkyd Enamel
Quick-Drying Styrenated Alkyd Paint

Alkyd Urea Clear Coat
Transparent Modified Alkyd Sealer
Alkyd Semigloss Finish
Transparent Modified Alkyd Sealer
Quick Drying Modified Alkyd Based Primer
Rust Preventing Primer
Quick Drying Clear Urethane Alkyd Varnish
Versatile Finish Coat Based On Long Oil Alkyd Resin Exceptionally Durable Fast Drying Alkyd Paint
Fast Dry Alkyd Metal Primer
Alkyd Gloss Enamel
High Gloss Alkyd Aluminum Paint
Alkyd Baking Enamel

  

High Gloss Alkyd Aluminum Paint

PRODUCT SPECIFICATIONS:

DESCRIPTION
A one pack, high gloss alkyd aluminum paint. Designed for interior/exterior use in mild industrial atmosphere for achieving water resistant bright finish and heat resistance up to 0 ºC.
RECOMMENDED USES
For use over prepared substrate such as steel, aluminum, galvanizing, and concrete block for decorative and industrial maintenance. Can be used for storage tanks, refineries, radiators, bridges, pipelines, and ducts.
CHARACTISTICS
Color:
Silver Bright
Finish:
Aluminum
Volume Solid:
41% +1%
Specific Gravity:
0.94 KGs / ltr + 2%
Recommended DFT:
50 Microns
Spreading Rate@DFT:
8. m 2 / ltr or
31.10 m2 / gallon
Flash Point:
30 oC
Drying Schedule:
@ 25 oC/R.H.50
Dry to Touch:
2 Hours
To Handle:
6 Hours
To Recoat:
12 Hours
Shelf Life:
18 months, unopened at 25 oC
Reducer/Clean Up:
Paint Thinner HJ-09
APPLICATION PROCEDURES
Surface Preparation:Surface must be dry, clean and in sound condition. Remove oil, dust, dirt, millscale or other foreign substance to ensure good adhesion. Minimum surface preparation methods to be followed for (1) Iron and Steel – SSPC-SP2 or SP3 (2) Aluminum and Galvanizing – SSPC-SP1 (3) Concrete should be cured, dry and clean. Allow weathering of new galvanized steel for six months prior to coating.
Application Methods:
Conventional Spray:
Reduce 5% with paint thinner
Airless Spray:
Reduce as required for suitable spray
Brush/Roller:
Reduction not recommended
SYSTEM RECOMMENDATION
Iron, Steel, Aluminum, Galvanized Steel:
Zinc Chromate Primer
1 Coat
50 Microns DFT
Industrial Aluminum Paint
2 Coats
50 Microns
DFT per coat
Iron and Steel (Self Prime):
Industrial Aluminum Paint
2 Coats
50 Microns
DFT per coat
Previously Painted Surfaces: Surfaces should be free from all foreign material. Old paint films must be brush blasted or scuff sanded prior to coating. Unknown old paint surface should be tested for lifting or peeling. If it does, clean to sound substrate and treat as new surface.

SPECIAL TIPS
Excessive reduction of material can affect the film build, appearance, and adhesion. Any further specific technical information can be obtained from www.polyurethane-paint.com
SAFETY PRECAUTIONS
Spray under well-ventilated conditions. Do not breathe or inhale mist. When spraying, wear air mask. Avoid skin contact. Spillage on skin should immediately be removed with suitable cleanser, soap and water. Eyes should be flushed with water and medical attention sought immediately.

 

 