Micaceous Iron Oxide Pigmented Two-Pack Epoxy Coating Supplier in China
Micaceous Iron Oxide Pigmented Two-Pack Epoxy Coating Coating paint coating manufacture Shenzhen China  
Home About Us Products Contact Us



Honest Joy Coating & Paint
Red Oxide Primer

Chlorinated Rubber Red Oxide Primer
Epoxy Micaceous Iron Oxide Coating
Micaceous Iron Oxide Pigmented Two-Pack Epoxy Coating
Modified Alkyd Based Anticorrosive Red Oxide Metal Primer
Drying Oil Gray Oxide Primer
Oil Red Oxide Primer
Red Oxide Rust Preventative Primer
Red Oxide Finish
Lead Free Red Oxide Primer
Red Oxide Quick Dry Primer


Micaceous Iron Oxide Pigmented Two-Pack Epoxy Coating

Product description
A high solids, low VOC, high build, micaceous iron oxide pigmented two-pack epoxy coating.
Recommended use
Exclusively as a high build MIO epoxy intermediate coat as a part of a multi layer coating system for protection of steel
structures. The intermediate coat is used to improve the barrier protection for anti corrosive coatings systems in a wide
range of environments.

Film thickness and spreading rate








Film thickness, dry (μm)




Film thickness, wet (μm)




Theoretical spreading rate (m²/l)




Physical properties


Red, Grey

Solids (vol %)*

82 ± 2

Flash point

25ºC ± 2


180 gms/ltr .



Gloss retention


Water resistance

Very good

Abrasion resistance

Very good

Solvent resistance

Very good



Surface preparation
All surfaces should be clean, dry and free from contamination. The surface should be assessed and treated in
accordance with .
Coated surfaces
Should only be applied over clean, dry and undamaged compatible anti-corrosive zinc primer. Zinc silicate primed
surfaces must be fully cured and free of zinc salts and contaminants.
Other surfaces
The coating may be used on other substrates.
Condition during application
The temperature of the substrate should be minimum 15°C and at least 3°C above the dew point of the air. The
temperature and the relative humidity should be measured in the vicinity of the substrate. Good ventilation is usually
required in confined areas to ensure proper drying. The coating should not be exposed to oil, chemicals or mechanical
stress until fully cured.
Application methods
Spray Use airless spray
Brush Recommended for stripe coating and small areas, care must be taken to achieve the specified dry
film thickness.

Application data


Mixing ratio (volume)

4 parts Comp. A (base) to be mixed thoroughly with 1 part Comp. B (curing agent)


5-10 minutes prior to use.

Pot life (23°C)

2 hours. (Reduced at higher temp.)


Honest Thinner No. 17 (up to 5% for lower film thickness application.)

Guiding data airless spray


 Pressure at nozzle

15 MPa (150 kp/cm², 2100 psi.)

 Nozzle tip

0.53 - 0.69 mm (0.021-0.027")

 Spray angle

40 - 80°


Check to ensure that filters are clean.

Drying time
Drying times are generally related to air circulation, temperature, film thickness and number of coats, and will be
affected correspondingly. The figures given in the table are typical with:
* Good ventilation (Outdoor exposure or free circulation of air)
* Typical film thickness
* One coat on top of inert substrate

Substrate temperature




Surface dry

6 h

4 h

2 h

Through dry

9 h

6 h

3 h


10 d

7 d

5 d

Dry to recoat, minimum

9 h

6 h

3 h

Dry to recoat, maximum 1




1. Provided the surface is free from chalking and other contamination prior to application, there is normally no
overcoating time limit. Best intercoat adhesion occurs, however, when the subsequent coat is applied before
preceding coat has cured. If the coating has been exposed to direct sunlight for some time, special attention must
be paid to surface cleaning and mattening/removal of the surface layer in order to obtain good adhesion.
The given data must be considered as guidelines only. The actual drying time/times before recoating may be shorter or
longer, depending on film thickness, ventilation, humidity, underlying paint system, requirement for early handling and
mechanical strength etc. A complete system can be described on a system sheet, where all parameters and special
conditions could be included.


1 x 60 μm

(Dry Film Thickness)

Penguard Midcoat MIO

1 x 175 μm

(Dry Film Thickness)

Hardtop AS/Hardtop XP

1 x 50 μm

(Dry Film Thickness)

Other systems may be specified, depending on area of use
The product must be stored in accordance with national regulations. Storage conditions are to keep the containers in a
dry, cool, well ventilated space and away from source of heat and ignition. Containers must be kept tightly closed.
Handle with care. Stir well before use.
Packing size
16 litres Comp. A (base) in a litre container and 4 litres Comp. B (curing agent) in a 5 litre container and
4 litres Comp. A (base) in a 5 litre container and 1 litres Comp. B (curing agent) in a 1 litre container.
Packing may vary from country to country according to local requirements.
Health and safety
Please observe the precautionary notices displayed on the container. Use under well ventilated conditions. Do not
breathe or inhale mist. Avoid skin contact. Spillage on the skin should immediately be removed with suitable cleanser,
soap and water. Eyes should be well flushed with water and medical attention sought immediately.
For detailed information on the health and safety hazards and precautions for use of this product, we refer to
the Material Safety Data Sheet.
The information in this data sheet is given to the best of our knowledge based on laboratory testing and practical
experience. However, as the product is often used under conditions beyond our control, we cannot guarantee anything
but the quality of the product itself. We reserve the right to change the given data without notice.