Polyester Coating

TGIC Free Polyester Powder Coating
Reinforced Trowel Applied Polyester Lining Topping
Polyester Thick Film Coating
Polyester Flake Coating

Polyester Resin Fast Setting Bedding Mortar
Polyester Baking Enamel
High Quality Acrylic Polyester Resin Basecoat
Free Glass Flake Reinforced Polyester Coating
Flowable Rapid Setting Polyester Resin Mortar
Flake Filled Polyester Coating
Durable Polyester Powder Coating

Clear Polyester Powder Coating
Abrasion Resistant Glass Flake Reinforced Polyester Coating
Abrasion Resistant Glass Flake Reinforced Polyester Coating




  

PRODUCT SPECIFICATIONS:

GENIC TYPE: Unsaturated polyester filled with inert pigments.
RECOMMENDED USAGE: Primarily used for lining tanks, coating process equipment and as an industrial maintenance material. It is easily applied to metal, concrete and wood.
CHEMICAL RESISTANCE GUIDE:
EXPOSURE IMMSION SPLASH & SPILLAGE
Acids Good Excellent
Alkalies Good Excellent
Petroleum
Products Good Good
Saltwater Excellent Excellent
Water Excellent Excellent
ORDING INFORMATION:
Shipping Weight:
HJ-1100 Approx 11 lbs/gal
S-311 Solvent Approx 8 1/lbs/gal
Packaging: HJ-1100 series is available
in 1 gallon and 5 gallon kits.
Flashpoint (T.C.C):
HJ-1100 73°F (23°C)
S-311 Solvent 73°F (23°C)
ORDING INFORMATION:
Shipping Weight:
HJ-1100 Approx 11 lbs/gal
S-311 Solvent Approx 8 1/lbs/gal
Packaging: HJ-1100 series is available
in 1 gallon and 5 gallon kits.
Flashpoint (T.C.C):
HJ-1100 73°F (23°C)
S-311 Solvent 73°F (23°C)
PHYSICAL DATA:
Solid by wt: approx 95%
Solid by vol: approx 93%
Note: Solids vary with color.
Pot life: 2 hrs @ 77°F
Shelf life: 12 months @ 70°F in
VISCOSITY: 100-110 K.U.
TEMPATURE LIMITATION: HJ-1100 accepts dry heat temperatures up to 2°F. Temperature excursions up to 400°F can be tolerated for short durations.
VOC: 0.5 lbs/gal as supplied.
STANDARD COLOR
hj-1101Red (Primer)
HCR-1110 White (Finish)
COVAGE: Theoretical coverage - 1488 sq ft per gallon per mil. At 35 mils DFT average coverage would be 34 sq ft per gallon. This includes a % loss factor. Recommended total DFT is as follows.
Environment DFT No. of Coats
Immersion 30-40 mils* 2*
*15- mils primer; 15- mils finish
SURFACE PREPARATION: Remove all oil, grease and other contaminants. All seams should be continuously welded, weld splatter removed and all edges radiused.
STEEL:
IMMSION: A white metal blast is required in accordance with SSPC-SP-5-63 specifications.
NON-IMMSION: A commercial blast is acceptable in accordance with NACE #3 or SSPC-SP-6-63 specifications.
Surface profile or anchor pattern shall be -25% of the recommended dry film thickness.
CONCRETE: Remove all protrusions by sanding or grinding. Concrete must be cured 28 days @ 70°F (21°C) and 50% relative humidity.
IMMSION: Dry abrasive blast to open all voids.
NON-IMMSION: Surfaces must be acid etched or abrasive blasted to remove laitance.
PRIM: hj-1101
MIXING: Stir Part A thoroughly. Add the contents of Part B to the container of Part A. Mix thoroughly. Mixed material must be used within 2 hours.
THINNING: The amount of thinner required is dependent upon temperature, ventilation, humidity; spray equipment used and desired film thickness. Suggested thinning at 75°F (24°C) is 15-%.
EQUIPMENT:
1. All spray equipment shall be thoroughly cleaned and be free of old paint and other contaminants.
2. Use standard production type spray guns
3. Air supply shall be uncontaminated.
4. Airless spray equipment: 2400-2800 PSI liquid pressure. Tip size from .015” to .019". Thinning requirements are less than for conventional spray.
SURFACE PREPARATION: Remove all oil, grease and other contaminants. All seams should be continuously welded, weld splatter removed and all edges radiused.
STEEL:
IMMSION: A white metal blast is required in accordance with SSPC-SP-5-63 specifications.
NON-IMMSION: A commercial blast is acceptable in accordance with NACE #3 or SSPC-SP-6-63 specifications.
Surface profile or anchor pattern shall be -25% of the recommended dry film thickness.
CONCRETE: Remove all protrusions by sanding or grinding. Concrete must be cured 28 days @ 70°F (21°C) and 50% relative humidity.
IMMSION: Dry abrasive blast to open all voids.
NON-IMMSION: Surfaces must be acid etched or abrasive blasted to remove laitance.
PRIM: hj-1101
MIXING: Stir Part A thoroughly. Add the contents of Part B to the container of Part A. Mix thoroughly. Mixed material must be used within 2 hours.
THINNING: The amount of thinner required is dependent upon temperature, ventilation, humidity; spray equipment used and desired film thickness. Suggested thinning at 75°F (24°C) is 15-%.
EQUIPMENT:
1. All spray equipment shall be thoroughly cleaned and be free of old paint and other contaminants.
2. Use standard production type spray guns
3. Air supply shall be uncontaminated.
4. Airless spray equipment: 2400-2800 PSI liquid pressure. Tip size from .015” to .019". Thinning requirements are less than for conventional spray.