Two Component Oxirane Ester Paint Containing Active Anti-Corrosive Pigments Supplier in China
Two Component Oxirane Ester Paint Containing Active Anti-Corrosive Pigments paint coating manufacture Shenzhen China  
Home About Us Products Contact Us

 

 




Honest Joy Coating & Paint
Other coating

Concrete Repair Coatings
Easy Sanding Clear Lacquer Sealer
Hydraulic Fluid Resistant Non-slip Finishes
Highly Reflective Marking Paint

Waterborne Thermosetting Glass Paint
Unsaturated Polyester Glass Flake Putty Coating Paint
Coating for Die Casting Aluminum Galvanize and Steel Parts
Semi-Transparent Organic Solvent Stain
Polyester Epoxy Coil Coating
Hard Abrasive And Weather-Resistant High Gloss Marine Varnish

Alkyd Urea Clear Coat
Concrete Aluminum And Steel Marine Structure Epoxy Coating
Zinc Rich Epoxy Powder Coating

Epoxy Powder Coating
Concrete Aluminum And Steel Marine Structure Epoxy Coating
Water Chemical Resistance Tin Lining Coating
Aqua-Loc Ceramic Topcoat
Removable Petroleum-Based Liquid Barrier Coating
Semi-Gloss Precatalyzed Lacquer
Premium High Build Precatalysed Timber Lacquer
Rapid Dry Gloss Enamel
Temperature Indicating Paint
Two Component Oxirane Ester Paint Containing Active Anti-Corrosive Pigments
Molybdenum Disulfide Slick Lubricant Coating

  

Two Component Oxirane Ester Paint Containing Active Anti-Corrosive Pigments

PRODUCT SPECIFICATIONS:

DESCRIPTION

A two component oxirane ester paint containing active anti-corrosive pigments.

PRODUCT FEATURES AND RECOMMENDED USES

 

  1. ♦ Used as a single coat or as a topcoat in oxirane ester based systems on steel surfaces exposed to abrasion and chemicals in severe climatic conditions.
  2. ♦ Excellent durability.
  3. ♦ Environmentally more friendly and for users more safe alternative than epoxy and polyurethane paints.
  4. ♦ High volume solids.
  5. ♦ High film build properties, up to 100 μm / one coat.
  6. ♦ Suitable for earth moving machines, haulage and lifting equipment, forklifts, agricultural machinery, electric appliances, pumps and other steel structures, equipment and machinery.

TECHNICAL DATA

Volume solids

approx. 65 ± 2 %.

Specific gravity

approx. 1.5 kg / l

Mixing ratio and product codes

Base 2 parts by volume 527-series
Hardener 1 part by volume 008 7675 (55904), other hardeners: see page 2

Pot life

8 hours (23 ºC)

Recommended film thicknesses and theoretical coverage

Recommended film thicknesses approx.
Theoretical coverage approx.
dry
wet
60 μm
95 μm
10.6 m2/l
100 μm
160 μm
6.4 m2/l
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.

Drying times

DFT 80 μm
+ 23 ºC
Dust dry, after
30 - 60 min
Touch dry, after
4 - 6 h
Dry to handle, after
8 - 12 h
Recoatable with other HJ-505 paints, after
a few min
Through dry at increased temperature after 45 min / 80 ºC.
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.

Finish

Varies depending on the used hardener. See page 2.

Colours

APPLICATION DETAILS


Surface preparation

Oil, grease, salts and dirt are removed by appropriate means.
Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.
Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer.

rimer

HJ PRIM and HJ-3032.

P

inish

HJ-3032.

F

Application conditions

All surfaces must be dry. The temperature of the ambient air, surface or paint itself should not fall below +10 ºC during application or drying. Relative humidity should not exceed 80 %. The surface temperature of the steel should remain at least 3 ºC above the dew point.

Mixing components

First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use Temaspeed Squirrel Mixer for mixing.

Application

By airless, conventional or electrostatic spray. At airless spray application the paint can be thinned if necessary to a viscosity of s . Airless spray nozzle tip "0.013 - 0.015", pressure ratio at least 30:1 and nozzle pressure 160 - 0 bar. Atomization air pressure 2 - 4 bar.
At conventional spray application the viscosity should be - 40 s and at electrostatic spraying s .
Properties and gloss of HJ-3032 will vary according to the used hardener:

Avoid hot spray!

hinner

HJ-148 or HJ-140.

T

leaning of equipment

HJ-148 or HJ-140.

C

VOC

The Volatile Organic Compounds amount is 3 g/litre of paint mixture.
VOC content of the paint mixture (thinned 15 % by volume) is 399 g/l.