Two-component Chemical Resistant Enamel

Surface Tolerant Self-priming Corrosion Inhibitor Coating
Structrial Steel Primer
Sovent Borne Alkali Resisting Primer
Solvent-borne Aluminium Finish
Solvent Based Anti-slip Floor Paint
Single Component Penetrating Corrsion Inhibitor
Single Component Industrial Maintenance Primer

Multifunctional Chemical Resistant Coating
Moisture Resistant Lacquer
Pipe Coating
Anti Static Coating
Anti-Static Conductive Primer




  

Two-component Chemical Resistant Enamel

PRODUCT SPECIFICATIONS:

DESCRIPTION:
Epoxy Polyamide Enamel is a high gloss, two-component chemical resistant enamel. Epoxy Enamel is for use on
primed or previously painted concrete, plaster, drywall, wood and metal surfaces such as walls, doors, trim, catwalks,
railings, storage tanks and machinery. Product is suited for high use areas of schools, office buildings and hospitals
where maximum durability and resistance to stains and washing is necessary. Product may be applied by brush, roller
or spray, however, brush is preferred.

SPECIAL CAUTIONS:
Do not apply when material, surface or air temperature is below 60°F. (15°C.).
SURFACE PREPARATION:
GENAL - Surface must be clean. Remove oil and grease with a detergent solution or paint thinner. Wash off dirt
with warm soapy water and rinse with fresh water. Rust should be removed by wirebrushing or sanding. Refer to
"Surface Preparation Guide" for more detailed instructions.
UNFINISHED INTIOR SURFACES:
WOOD, PLYWOOD, HARDBOARD, PARTICLE BOARD AND OTH WOOD DIVATIVES - Surface must be
clean and dry. Prime with primer undercoat and allow to dry overnight before topcoating.
MASONRY-POURED AND PRE-STRESSED CONCRETE - Surfaces should be clean and dry. Etch all surfaces with
a mixture of 2 parts water and 1 part muriatic acid. After etching action stops, wash the surface thoroughly with fresh
water and allow to dry. Fill all pits and air holes with Latex-Cement Patching Compound. Allow to cure overnight. If
the concrete has not aged, prime with latex primer and allow to dry at least two hours before topcoating.
BLOCK-CONCRETE, HAYDITE, AGGREGATE - Be sure surface is clean and free of mud, dirt, dust or other foreign
matter. Cracked joints or blocks should be repaired.
Normal Service - Dry with Occasional Splash and Spillage. Surface should be filled with latex block filler. Avoid the
formation of a layer of filler on the block face. Allow block filler to dry overnight before topcoating.
Severe Service - Continually High Moisture Areas - Surface should be filled with epoxy block filler. Allow block filler to
dry overnight before topcoating.
PLAST AND WALLBOARD - Surface must be clean and dry. Prime with latex primer and allow to dry overnight.
ASBESTOS-CEMENT BOARD, BRICK AND UNGLAZED TILE - Surface must be clean and dry. As a first coat on
dense cementious surfaces, such as poured concrete, asbestos cement board and unglazed tile, thin the first
application of Epoxy with one pint of Epoxy Reducer per mixed gallon.
IRON AND STEEL - Commercial Sandblast SSPC No. 6 is preferred for maximum adhesion and durability. Power
Tool SSPC No. 3 is minimum requirement for surface preparation. Prime with one application of epoxy primer. Allow
overnight dry before topcoat.
GALVANIZED METAL & ALUMINUM - Surface must be clean and dry. Solvent Wash SSPC No. 1 recommended
prior to application of epoxy primer. Allow overnight dry before topcoat.
MIXING:
Mix equal parts of Epoxy Enamel with catalyst. Allow mixed unit to stand for 30 minutes before using. Pot life of
mixed unit is approximately 8 hours at 75°F. (26°C.). Mix no more material than will be needed for use in one working
day. Small quantities of mixed Epoxy may be stored under refrigeration (40°F. or less) for not more than 24 hours.
Apply at package viscosity.
APPLICATION:
Do not apply when either surface, air or material temperature is below 60° F. (15°C.). Epoxy may be applied by brush,
roller or by conventional or airless spray application.
To spray, use the following recommendation or equal as a guide:
AIRLESS SPRAY:
Tip . . . . . . . . . . . . . . . .013-.015"
Fan . . . . . . . . . . . . . . 50°-60° (10-12 inch fan)
Pressure . . . . . . . . . . 1800-00 PSI
CLEAN UP:
Clean brushes, rollers and spray equipment, immediately after each use, with Epoxy Reducer. Dispose of used paint
and waste in accordance with local, state and federal regulations.
COVAGE:
One gallon of converted Epoxy should be applied at application rate of 400 square feet per gallon (37 square meters
per 3.785 liters) on smooth surfaces. Approximate dry mil thickness of 2 mils at application rate of 400 square feet per
gallon.
DRYING:
Optimum drying conditions are 60° F. to 90° F. (16° C. to 32° C.) at 50% R.H.
To Touch . . . . . . . . . . . . . . 2 Hours
To Recoat . . . . . . . . . . . . . . Overnight
Full Cure . . . . . . . . . . . . . . . 5-7 Days
Lower temperatures and high humidity will slow dry.
DESCRIPTION:
Epoxy Polyamide Enamel is a high gloss, two-component chemical resistant enamel. Epoxy Enamel is for use on
primed or previously painted concrete, plaster, drywall, wood and metal surfaces such as walls, doors, trim, catwalks,
railings, storage tanks and machinery. Product is suited for high use areas of schools, office buildings and hospitals
where maximum durability and resistance to stains and washing is necessary. Product may be applied by brush, roller
or spray, however, brush is preferred.
Values based on Epoxy Polyamide Gloss Enamel White,HJ-005 (mixed)
Weight Gallon: 12.16
Weight Solids: 69.9%
Volume Solids: 50.7%
Coverage:
@ 1 Dry Mil: 813 sq. ft./gallon
@ Spread Rate: 400 sq. ft./gallon (4.0 mils wet)
Deposits a 2.0 mil dry film
VOC (g/l): Not to Exceed 450
Viscosity: 70-80 K.U. @ 77° F.
Gloss @ 60: 90+
Grind (Hegman): #6.5-7
DOT Class: Flammable, Flash Point 81°F.
Specification: Performance Alternate
/NFPA: 2,3,0
Cure Time (Based on 70° F. & 50% R.H.):
To Touch: 2 Hours
To Recoat: Overnight
Recommended Thinner: None. Apply at package viscosity. Epoxy Reducer for clean-up.
Temperature Resistance: Continuous 150° F., Intermittent 0° F.
CAUTION! Keep away from heat and open flame. Avoid prolonged contact with skin and breathing of vapor or spray
mist. Do not take internally. Close container after each use. Use only with adequate ventilation. KEEP OUT OF
REACH OF CHILDREN. For specific safety requirements, refer to the Material Safety Data Sheet.
LIMITATION OF LIABILITY: To the best of our knowledge, the technical data contained herein is true and accurate at the date of
issuance, but is subject to change without prior notice. We make no guarantee of any kind, express or implied, including
merchantability and fitness for particular purposes. Liability, if any, is limited to replacement of the product or refund of the
purchase price. Labor, or cost of labor, and other consequential damages are hereby excluded.

 



Contact Us
 
Honest Joy Coating & Paint. All rights reserved.