Water Chemical Resistance Tin Lining Coating Supplier in China
Water Chemical Resistance Tin Lining Coating paint coating manufacture Shenzhen China  
Home About Us Products Contact Us

 

 




Honest Joy Coating & Paint
Other coating

Concrete Repair Coatings
Easy Sanding Clear Lacquer Sealer
Hydraulic Fluid Resistant Non-slip Finishes
Highly Reflective Marking Paint

Waterborne Thermosetting Glass Paint
Unsaturated Polyester Glass Flake Putty Coating Paint
Coating for Die Casting Aluminum Galvanize and Steel Parts
Semi-Transparent Organic Solvent Stain
Polyester Epoxy Coil Coating
Hard Abrasive And Weather-Resistant High Gloss Marine Varnish

Alkyd Urea Clear Coat
Concrete Aluminum And Steel Marine Structure Epoxy Coating
Zinc Rich Epoxy Powder Coating

Epoxy Powder Coating
Concrete Aluminum And Steel Marine Structure Epoxy Coating
Water Chemical Resistance Tin Lining Coating
Aqua-Loc Ceramic Topcoat
Removable Petroleum-Based Liquid Barrier Coating
Semi-Gloss Precatalyzed Lacquer
Premium High Build Precatalysed Timber Lacquer
Rapid Dry Gloss Enamel
Temperature Indicating Paint
Two Component Oxirane Ester Paint Containing Active Anti-Corrosive Pigments
Molybdenum Disulfide Slick Lubricant Coating

  

Water Chemical Resistance Tin Lining Coating

PRODUCT SPECIFICATIONS:

DESCRIPTION:  

Epoxy Phenolic coating is a cross-linked epoxy-phenolic, high performance coating capable of providing economical protection in severe and chemically corrosive environments.

RECOMMENDED USAGE:

Tank linings, heat transfer equipment, spiral heat exchangers, fans, blowers, filter plates, tank cars, tank trailers, duct work, exhaust hoods, and other industrial equipment.

TECHNICAL DATA

Dry to touch:

≤1.0h

Recoat interval, min 

(4-8)h

Hard dry

(180-0)℃×(1.0-1.5)h

Flexibility

1mm

Impact resistance

50cm

Hardness

0.7

Adhesion

≤1grade

Minimum Coverage

0.08-0.10kg/m2/coat, it can be adjusted according to the demands.

Theoretical Coverage:

Primer

0.14-0.17kg/m2

Topcoat

0.13-0.15kg/m2

Recommended dry film thickness:

Primer

45μm×1 coat;

Topcoat

45μm×2 coat.

Theoretical coverage:

Primer

6.2m2/kg/coat(8.7 m2/L/coat)、

Topcoat

6.2 m2/kg/coat(8.7 m2/L/coat)

Flash point

≥23℃

Pot life, h

≥8

Sulfuric acid resistance(30%), 480h:

no foaming and falling off 

Sodium hydroxide resistance(30%), 480h:

no foaming and falling off 

Water resistance, 480h

no foaming and falling off 

Toluene resistance, 480h

no foaming and falling off 

Acetone resistance, 480h:

no foaming and falling off 

Heat resistance, 0℃×24h:

no foaming and falling off 

SURFACE PREPARATION:

Remove all oil, grease and other contaminants with an appropriate solvent, or thinner.

STEEL:

Surface profile or anchor pattern shall be -25% of the recommended dry film thickness.
IMMSION:

A white metal blast is required in accordance with SSPC-5 specifications.

NON-IMMSION:

A commercial blast is acceptable in accordance with NACE # 3 or SSPC-6 specifications

PRIM:

Not required.

MIXING:

Mix thoroughly; making sure all settled pigments are re-dispersed.

THINN & CLEAN UP SOLVENT:
.
THINNING:

The amount of thinner required is dependent upon temperature, ventilation, humidity; spray equipment used, and desired film thickness. Adjust viscosity to 30 to 40 . Suggested thinning is 10-40% at 75°F (24°C).

APPLICATION:

  1. Do not apply if temperature is less than 5°F (2°C) above dewpoint, or if temperature is below 45°F (7°C).
  2. All spray equipment shall be thoroughly cleaned and the hoses in particular shall be free of old paint film and other contaminants.
  3. Use standard production type spray guns.

Airless spray equipment, 1800-20 PSI liquid pressure. Tip size from .013" to .019".

  1. Air supply shall be uncontaminated. Adjust air pressure to approximately 80 lbs. at the gun and provide 15- lbs. pot pressure. Adjust spray gun by first opening liquid valve and then adjust air valve to give approximately an 8" to 12" fan holding gun perpendicular to the surface at a distance of 12".
  2. Apply a mist bonding pass. Allow to flash off for several minutes but not long enough to allow film to completely dry.
  3. Apply 3-4 cross-cross multi-passes maintaining a wet appearing film approximately 3-4 mils. Wet film thickness equals 1.5-2.0 mils dry film thickness.
  4. Air dry approximately 1 hour with ventilation, prior to introducing heat.
  5. After the air dry period has elapsed, the temperature should be raised approximately 40°F (22°C) in increments of 30 minutes until the desired temperature is reached.  

STORAGE CONDITIONS:

    • Coating should not be stored longer than 12 months at 70°F (21°C).
    • Keep all containers tightly closed during storage. For further storage after opening, containers must be purged with nitrogen gas or dry air and tightly sealed to protect from moisture contamination.
    • Store drums and pails in a cold, dry and ventilated location
    • Keep away from rain and sun
    • Keep away from fire and heat source

     

     

     