Water Reducible Enamel
Water Miscible Epoxy Coating
Water Borne Inorganic Zinc Rich Silicate Primer
Two-Component Water-Borne Epoxy Primer

Water Based Two-Component Epoxy Polyamide Finish
Water-Borne High Performance Acrylic Metal Primer
Water Based Gloss Epoxy Enamel

Urethane Modified High Solids Water Borne Coating
Water-Borne High Performance Acrylic Metal Primer
Water Borne Acrylic Protective Coating
Arylic Thermo Plastic Waterbase Finish
Self-Levelling Epoxy Flooring Water Borne
Acrylic Water borne Paint Eggshell Waterborne Interior Paint
Environmentally Friendly Waterborne Metal Primer
Fast Drying Interior Exterior Primer
Acrylic Water borne Paint
High Gloss Waterborne Aliphatic Polyurethane Enamel


Water Reducible Enamel


A solvent free, water dispersible polyisocyanate. It provides outstanding coverage, excellent
durability, and ease of application as well as being a low VOC and EPA compliant coating.
Polyurethane Topcoat offers superior adhesion and has film properties that exceed most solvent based catalyzed. It does not contain lead
or chromates. The solid and semi-solid sludge produced in spraying and clean up can be
flocculated, dried and sent to a "Class B" landfill. Check your local and state regulations for
proper handling.

• Excellent exterior durability
• Non-photo chemically reactive
• Full gloss – 92% at 60o glossometer
• Available in satin to gloss finish
• Excellent hardness/impact resistance
• Excellent adhesion, mar, and abrasion resistance
• Coating will not flash rust on clean dry metals
• Coatings can be applied in a wide range of temperature and humidity conditions
without the use of retarders
• Linear flexibility is excellent on substrates such as Lexan, vinyl, and fiberglass
• Excellent retention of gloss in 1000 hour QUV weatherometer
• deionized water is used for reduction
• Excellent performance on structural plastics
• Water is used for clean-up
• Non-Hazardous
• Wide range of colors
• Shelf life - 1 year
• Non-Flammable
• Metallics can be formulated
• Steel, Steel Decks, Aluminum • Plastics
• Vinyl • Concrete
• Fiberglass • Canvas
• Wood • Polyester Fabric

• VOC (Volatile Organic Compounds) 0.23 lb/gal, 27 gm/lt. when catalyzed
VOC’s Part A: 0.0 LB/gal, 0.0 gm/lt
VOC’s Part B: 0.9 LB/gal, 108 gm/lt
• Free of lead and chromates
• Non-photo chemically reactive
• Liquid, clear
• Specific Gravity: >1
• Vapor Density: Heavier than air
• Evaporation Rate: Slower than ether
• VOC: 0.3 lb/gal, 36 gm/lt
• Boiling Point: 340oF (171oC)
• % Solids by weight: 47% when catalyzed
• % Solid by volume: 50% when catalyzed
• Weight per gallon: 9.4 lbs.
• Flash Point: 320oF CC
The tests below were conducted on aluminum panels at 1-1.5 mil dry film thickness after 14
days cure time at a room temperature of 77oF (25oC). Each test rated excellent or no failure.
• Salt Spray: 1000 hours
• Solvent Resistance: lacquer thinner, acetone, MEK, gasoline, xylene-100 double
rubs with saturated cloth.
• Pencil hardness test to 4H
• Flexibility: 1/8" conical mandrel
• Impact Resistance: Forward: 180 inch pound, Reverse: 180 inch pounds
• Taber Abrasion: CS17 wheel, 1,000 gm load (100mg loss/1,000 cycles) • Theoretical Coverage at 1 mil: 812 ft2 (1624 x 50% solids by volume)
• Gloss Retention: >90% gloss retention after 1000 hours QUV (Quantitative
Ultraviolet light)